Some alloys don’t like to be melted. If an alloy has a large solidification range, certain areas can partially solidify without the liquid part keeping up to fill in the gaps so to speak. This leads to solidification cracking / hot tearing. This is a simplification and only one possible cause, but there are literal books written about this kind of thing (I like Solidification by Dantzig and Rappaz). This is also why you see things like friction stir welding for rocket bodies. No melting means no solidification means no solidification issues.